Die operations and types

Die operations and types

Die operations are often named after the specific type of die that performs the operation. For example a bending operation is performed by a bending die. Operations are not limited to one specific die as some dies may incorporate multiple operation types:

Bending:

The bending operation is the act of bending blanks at a predetermined angle. An example would be an "L" bracket which is a straight piece of metal bent at a 90° angle. The main difference between a forming operation and a bending operation is the bending operation creates a straight line bend (such as a corner in a box) as where a form operation may create a curved bend (such as the bottom of a drinks can).


Blanking:

A blanking die produces a flat piece of material by cutting the desired shape in one operation. The finish part is referred to as a blank. Generally a blanking die may only cut the outside contour of a part, often used for parts with no internal features.Three benefits to die blanking are:


1. Accuracy. A properly sharpened die, with the correct amount of clearance between the punch and die, will produce a part that holds close dimensional tolerances in relationship to the parts edges.

2. Appearance. Since the part is blanked in one operation, the finish edges of the part produces a uniform appearance as opposed to varying degrees of burnishing from multiple operations.

3. Flatness. Due to the even compression of the blanking process, the end result is a flat part that may retain a specific level of flatness for additional manufacturing operations.

Broaching: The process of removing material through the use of multiple cutting teeth, with each tooth cutting behind the other. A broaching die is often used to remove material from parts that are too thick for shaving.

Bulging: A bulging die expands the closed end of tube through the use of two types of bulging dies. Similar to the way a chefs hat bulges out at the top from the cylindrical band around the chefs head.

1. Bulging fluid dies: Uses water or oil as a vehicle to expand the part.
2. Bulging rubber dies: Uses a rubber pad or block under pressure to move the wall of a workpiece.

Coining: is similar to forming with the main difference being that a coining die may form completely different features on either face of the blank, these features being transferred from the face of the punch or die respectively. The coining die and punch flow the metal by squeezing the blank within a confined area, instead of bending the blank. For example: an Olympic medal that was formed from a coining die may have a flat surface on the back and a raised feature on the front. If the medal was formed (or embossed), the surface on the back would be the reverse image of the front.

Compound operations: Compound dies perform multiple operations on the part. The compound operation is the act of implementing more than one operation during the press cycle.

Compound die: A type of die that has the die block (matrix) mounted on a punch plate with perforators in the upper die with the inner punch mounted in the lower die set. An inverted type of blanking die that punches upwards, leaving the part sitting on the lower punch (after being shed from the upper matrix on the press return stroke) instead of blanking the part through. A compound die allows the cutting of internal and external part features on a single press stroke.